additives question...hardening pre-fired glazed surfaces

updated mon 31 jan 05

 

Saultman.com on sat 29 jan 05


Hi Everyone,

What is the best additive to minimize marring glazed surfaces while
handling.
I have read several descriptions of products but none address the
hardening issue.
Flocs?, APTII? These products seem to provide suspension and glaze flow
improvements but do not talk about hardening the chalky glaze surface.
Is there a protective "dip" that can be done to protect a glazed
surface yet allow additional layers to be added?

Dan Saultman

Rick Hamelin on sat 29 jan 05


VeeGum Cer is used for this purpose. Contains clay and magnesium. Use up to 1 1/2 percent
Rick

--
"Many a wiser men than I hath
gone to pot." 1649

-------------- Original message --------------

> Hi Everyone,
>
> What is the best additive to minimize marring glazed surfaces while
> handling.
> I have read several descriptions of products but none address the
> hardening issue.
> Flocs?, APTII? These products seem to provide suspension and glaze flow
> improvements but do not talk about hardening the chalky glaze surface.
> Is there a protective "dip" that can be done to protect a glazed
> surface yet allow additional layers to be added?
>
> Dan Saultman
>
> ______________________________________________________________________________
> Send postings to clayart@lsv.ceramics.org
>
> You may look at the archives for the list or change your subscription
> settings from http://www.ceramics.org/clayart/
>
> Moderator of the list is Mel Jacobson who may be reached at melpots@pclink.com.

John Britt on sat 29 jan 05


Dan,

CMC can help too.

Hope it helps,

John Britt
www.johnbrittpottery.com

bonnie staffel on sun 30 jan 05


I have written this before and it always seems to raise questions. I add
1/4 or 1% powdered CMC to the dry ingredients of my glaze before adding the
material to hot water. It provides a hard surface on which I can paint with
watercolor effects using glazes and Mason Stains without any powdery
residue. I use less water also as the glaze becomes deflocculated. The CMC
does not mold in this glaze that sits for a period of time in a laundry tub
between glaze sessions.

You can see my painterly techniques on a few of my older pieces, landscapes
and face plates. I have practiced this for many years.

Regards,

Bonnie Staffel

http://webpages.charter.net/bstaffel/
http://vasefinder.com/bstaffelgallery1.html
Charter Member Potters Council