Ababi on sat 18 may 02
Started far away with a recipe of Marty Anderson
DEEP YELLOW STABLE
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Cone 6 1222 deg.C. -
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Dolomite 19.00
EPK Kaolin 26.00
SILICA 39.00
FRIT VO 6004p 12.00
Calcium Carbonate 4.00
Titanium Dioxide 16.00
granular Rutile 4.00
Rutile 4.00
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Seger Weight%
KNO 0.150 2.97%
CaO 0.544 7.81%
MgO 0.306 3.16%
Al2O3 0.357 9.32%
B2O3 0.157 2.81%
SiO2 3.352 51.62%
TiO2 1.079 22.08%
K2O 0.071 1.71%
Na2O 0.080 1.27%
Al:Si 9.39
Expan. 8.01
ST 374.39
The huge amount of TiO2 and rutile are result of a blessed test where I
added too muchs as a result of too many tests on that day. You can get
a similar color with 8 titanium and 4 rutile. The mottling with the
granular rutile was kind of ugly sand.
It passed the freeze hot water the and soda test sightly leached. I
am not sure it matters. This glaze, I think should be thin on mottled
claybody or on clay like calico or his brother from Amaco where some
parts of the claybody are seen otherwise just yellow nice but boring
FRIT VO 6004 p......
========
100.00
K2O 0.47* 15.50%
Na2O 0.53* 11.50%
Al2O3 0.10 3.50%
B2O3 1.05 25.50%
SiO2 2.09 44.00%
Si:Al 21.35
SiB:Al 32.03
Expan 12.13
Ababi Sharon
Kibbutz Shoval- Israel
Glaze addict
ababisha@shoval.org.il
http://members4.clubphoto.com/ababi306910/
http://www.milkywayceramics.com/cgallery/asharon.htm
SusanRaku@AOL.COM on sun 19 may 02
>From Cerere@msn.com
> FRIT VO 6004p
What is this frit? What can be used as a substitute.
Thanks.
Ababi on mon 20 may 02
Frit 6004, as far as I know manufacture in Italy by a German company
and the only near substitute is made by Fusion> Tom Buck wrote me once
they sold it in big amounts.
For general knowledge http://www.cct.es/welcome.htm
As this recipe is built out of American recipe I will convert it for
you.
DEEP YELLOW STABLE CLAYART
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Cone 6 1222 deg.C. -
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Dolomite 19.00
EPK Kaolin 23.00
SILICA 33.00
FRIT 3195 12.00
FRIT 3110 12.00
Wollastonite 1.00
Titanium Dioxide 16.00
granular Rutile 4.00
Rutile 4.00 You can use 8.00 powder rutile
instead the way I made
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Seger Weight%
KNO 0.158 2.66%
CaO 0.543 7.95%
MgO 0.299 3.14%
Al2O3 0.358 9.51%
P2O5 0.001 0.05%
B2O3 0.151 2.75%
SiO2 3.336 52.31%
TiO2 1.037 21.62%
K2O 0.013 0.32%
Na2O 0.145 2.34%
Al:Si 9.33
Expan. 8.00
ST 373.80
Ababi Sharon
Kibbutz Shoval- Israel
Glaze addict
ababisha@shoval.org.il
http://members4.clubphoto.com/ababi306910/
http://www.milkywayceramics.com/cgallery/asharon.htm
---------- Original Message ----------
>From Cerere@msn.com
>> FRIT VO 6004p
>What is this frit? What can be used as a substitute.
>Thanks.
>________________________________________________________________________
>______
>Send postings to clayart@lsv.ceramics.org
>You may look at the archives for the list or change your subscription
>settings from http://www.ceramics.org/clayart/
>Moderator of the list is Mel Jacobson who may be reached at
>melpots@pclink.com.
| |
|